Abstract
In system level electromigration test of 2.5D integrated circuits, a failure mode due to synergistic effect of Joule heating and electromigration has been found. In the test circuit, there are three levels of solder joints, two Si chips (one of them has through-Si-via), and one polymer substrate. In addition, there are two redistribution layers; one between every two levels of solder joints. We found that the redistribution layer between the flip chip solder joints and micro-bumps is the weak-link and failed easily by burn-out in electromigration test. The failure is time-dependent with sudden resistance increase. Preliminary simulation results show that Joule heating has a positive feedback to electromigration in the redistribution layer and caused the thermal run-away failure. Joule heating becomes an important reliability issue in the future scaling of semiconductor devices.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.