Abstract
Abstract The heat-affected zone (HAZ) of reactor pressure vessel (RPV) steels is known to show large scatter in Charpy impact properties because it has inhomogeneous microstructure due to thermal histories of multi-pass welding for butt-welded joints. The correlation between mechanical properties and microstructure such as grain size, phase-fraction, martensite-austenite constituent, on the characteristics of HAZ of un-irradiated materials was investigated. Neutron irradiation was conducted at Japanese Research Reactor −3 (JRR-3) operated by JAEA. The neutron irradiation susceptibility was evaluated based on post-irradiation examinations consisting of mechanical testing and microstructural analysis. In the experiments, typical RPV steel plate and their weldment were prepared. Simulated HAZ materials that have representative microstructures such as coarse-grain HAZ (CGHAZ) and fine-grain HAZ (FGHAZ) were also prepared based on the thermal histories calculated by finite element analysis. For un-irradiated materials, a part of simulated HAZ materials showed a higher reference temperature of the master curve method than that of the base metal (BM). The irradiation hardening of HAZ was almost the same or lower than that of the BM, and the shift of reference temperature for HAZ materials was comparable with that of BM.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.