Surface treatment effects on morphological and property enhancements of poly (3‐hydroxybutyrate‐co‐3‐hydroxyvalerate)/Diss fibers (Ampelodesmos mauritanicus) biocomposites

Abstract

AbstractThe present research investigates the influence of chemical modifications on the surface of Diss fibers (Ampelodesmos mauritanicus) as an effective reinforcing agent for biocomposites based on poly (3‐hydroxybutyrate‐co‐3‐hydroxyvalerate) (PHBV). The Diss fiber surface underwent three different chemical treatments: alkaline, alkaline/peroxide, and alkaline/silane. Changes in morphology, mechanical properties, thermomechanical behavior, and contact angle measurements of the biocomposite materials were studied according to the following weight ratio PHBV/Diss fibers 80/20. Scanning electron microscopy (SEM) analysis of the fractured surface of the biocomposite samples revealed improved adhesion between Diss fibers and the PHBV matrix after surface modification, compared with the unmodified sample. The study demonstrated that the incorporation of Diss fibers leads to an enhancement in the mechanical performances of PHBV‐based biocomposites. The tensile properties of the modified biocomposites showed a significant increase in Young's modulus compared with the biocomposites with untreated fiber. Similar trends were observed in the data obtained from dynamic mechanical analysis (DMA) and contact angle measurement. Overall, the study highlights the beneficial effects of Diss fibers modification, particularly with the alkali–silane combination, in enhancing the properties of PHBV biocomposites, there by broadening their potential application fields.Highlights The study explores the potential of Diss fibers as an effective reinforcement for PHBV‐based biocomposites. Fully biodegradable biocomposites based on PHBV/Diss fibers are melt‐compounded. Diss fibers are chemically modified by alkaline, alkaline/peroxide, and alkaline/silane. The chemical treatment has considerably enhanced the properties and morphology of the biocomposites, being however much higher for alkaline/silane treatment. The method can be used for specific applications and large‐scale production.