AbstractThe changes in surface topography of thin metallic films during ion bombardment were investigated with STM. Pd and Au thin films, having defect-free, atomically flat areas over at least 300×300Å2 were bombarded with Ar+, Kr+, Xe+ ions. Ion energies and target temperatures were varied. The roughening after high fluence irradiation shows scaling with a roughness exponent 0.84. For 300 K target temperature we observe, both for Au and Pd, 3 D erosion, for 700 K, on the contrary, layer-by-layer erosion. The differences in erosion morphologies between Au and Pd surfaces are supposed to stem from differences in surface mobility of adatoms.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.