Abstract
The article presents selected issues related to material quality manufactured by selective laser sintering of AlSi10Mg alloy powder after milling. The workpiece was prepared and machined by down-milling and up-milling with tools made of high-speed steel. Breaches, pores and failure-like cracks on the machined surface were found, which negatively influenced the values of 3D surface roughness parameters. The occurring phenomena were analyzed and proposals for their explanation were made. The results of this research describe the effect of cutting parameters (the feed rate of f = 0.013–0.05 mm/tooth) on the values of parameters describing the surface quality and benchmarks. Topography measurements and 3D surface roughness parameters are presented, as well as the results of microscopic surface analysis. It was found that for aluminum alloy produced by the direct metal laser sintering (DMLS) method, the recommended machining method is down-milling.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.