Abstract
Surface tension of a polymer melt in a supercritical fluid is a principal factor in determining cell nucleation and growth in microcellular foaming. This work focuses on the surface tension of a crystalline polymer, high density polyethylene (HDPE), in supercritical nitrogen under various temperatures and pressures. The surface tension was determined by Axisymmetric Drop Shape Analysis-Profile (ADSA-P). The dependence of the surface tension on temperature and pressure, at temperatures above the HDPE melting point, ∼125 °C, was found to be similar to that of the amorphous polymer polystyrene (PS) in supercritical CO 2, previously reported, i.e., the surface tension decreased with increasing temperature and gas content. Below 125 °C and above 100 °C, HDPE underwent the process of crystallization, where the surface tension dependence on temperature was different from that above the melting point, and decreased with decreasing temperature. Differential scanning calorimetry (DSC) characterization of the polymer was carried out to reveal the process of HDPE crystallization and relate this to surface tension behavior. It was found that the amount of the decrease in surface tension was related to the rate of temperature change and hence the extent of polymer crystallization.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Colloids and Surfaces A: Physicochemical and Engineering Aspects
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.