Abstract
Fluoroelastomers are frequently used as engine oil-seal materials. Under certain test conditions specific fluoroelastomers may show degradation of mechanical properties. A range of fluoroelastomers of different chemical composition have been aged in simple oil/additive blends and in oil formulations equivalent to commercial blends. These were then examined using XPS, SEM/EPMA and XRD to elucidate the physical and chemical changes associated with degradation. The interaction is shown to proceed through amine catalysed post-curing of the constituent polymers. These reactions promote defluorination, embrittlement and cracking of elastomers with a consequent decline in tensile properties as fracture failure mechanisms dominate performance. Degradation of these materials was found, even in the most extreme case, to be limited to the near-surface region of the samples, to a depth of less than approximately 50 μm. Degradation was reduced in elastomers with a higher fluorine level, higher terpolymer content, and a greater extent of cross-linking.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.