Abstract
In this paper we analyze the surface structure and properties of high-chromium steel (steel 420) irradiated with a submillisecond (0.45 ms) intense pulsed electron beam on the COMPLEX vacuum setup at an Ar pressure of 3⋅10−2 Pa. The analysis suggests that electron beam treatment with surface melting dissolves the initial carbide phase in the steel, saturates its surface layer with Cr and C atoms, and form dendrites and martensite structure. The microhardness and the wear resistance of the irradiated steel are respectively 1.5 and 50 times higher compared to the initial material, and their maximum values are attained at a beam energy density of 53 J/cm2.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.