Abstract
The bainite transformation was studied by examining the surface distortions of various steels during thermal treatments. The relation between the relief structure and etched structure was also discussed. The results are follows: (1) Relief markings were observed during bainite transformation but pearlite did not produce any relief effect. (2) Each relief marking corresponds to the dotted line of carbide in the upper bainte structure and to the acicular structure of the lower bainite. (3) The relief marking due to bainite formation grows slowly and the rate of growth increases as the transformation temperature increases. The calculated value of the activation energy for the growth of the relief marking was about 19,000 cal/mol. (4) The growth rate of the relief marking at constant temperature was independent of the time of transformation. (5) The Widmannstätten figures of ferrite of various carbon and alloy steels produced distinct relief effects.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: Journal of the Japan Institute of Metals and Materials
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.