Abstract
The surface reconstructions of AlAs(100) layers grown by molecular beam epitaxy (MBE) on GaAs(100) were mapped as a function of substrate temperature and arsenic flux. Three main reconstructions were observed - a c(4 × 4) at lower temperatures and higher arsenic fluxes, a (2 × 4) at middle temperatures, and a (3 × 2) at higher temperatures and lower arsenic fluxes. Growth of AlAs on AlAs(100) is layer-by-layer for the high temperature and low temperature reconstructions. In the mid-temperature region, AlAs grows rough on (2 × 4) reconstructed AlAs(100) as indicated by rapidly damped reflection high-energy electron diffraction (RHEED) intensity oscillations and the appearance of three-dimensional (3D) features. The addition of fractional layers of Ga enhances the smooth growth of AlAs. A metastable (5 × 2) reconstruction was observed when a fraction of a layer of Ga was present on the surface. The results indicate that Ga segregates during the growth of AlAs on GaAs(100) at temperatures at least as low as 500°C, and that annealing at temperatures above 700°C removes most of the Ga from the surface.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.