Surface Reconstruction of High-Voltage LiNi0.5Mn1.5O4 Cathode via the Sculpture Method toward Enhanced Stability.

Abstract

High-voltage LiNi0.5Mn1.5O4 (LNMO) cathodes suffer from severe capacity degradation during long-term cycling due the manganese dissolution and their high operating voltage (∼4.95 V), which pose serious challenges at the surface or interface. Moreover, both traditional ion-doping and passivation layer coating are difficult to apply consistently to LNMO cathode because of their complicated procedures, especially in large-scale production. To address these issues, a strategy employing HNO3/H2O2 leaching in synergy with a sintering process at a mid-temperature of 700 °C was used to achieve selective surface reconstruction. An optimal ratio of reactants was applied to balance the capacity and the cyclic stability of the LNMO cathode. The optimized valence composition of Mn on the material surface mitigates the occurrence of Jahn-Teller distortion, accompanied by a reasonable ratio of ordered and disordered phases and the concentration of oxygen vacancies after sintering, which improves the interface behavior between the electrode and electrolyte. This method delivers a high reversible capacity of 116.5 mAh g-1 after 200 cycles at 0.5 C (1 C = 147 mAh g-1) with a capacity retention of 91.30% and 110 mAh g-1 with a remarkably high capacity retention of 86.85% after 500 cycles at 2 C. This balanced approach, utilizing the protective effects of oxidation (O22-) and the erosive action of acid (H+), is proposed to achieve regional surface reconstruction of advanced LNMO cathode. This opens up a strategy for improving oxide-based cathode materials with low cost and mass production capability, especially favoring high consistency.