Abstract
The surface properties of melamine-urea-formaldehyde (MUF) impregnated paper decorative panels are unsatisfactory, characterized by brittle surfaces, poor abrasion resistance, and limited flame retardancy. A modification was introduced to the MUF resin by incorporating a blend of polyelectrolyte complex polyethyleneimine (PEI)-phytic acid (PA) and Nano-Al2O3 with the aim of enhancing the surface properties of the decorative panel. The modified resin underwent characterization, and subsequent analyses were conducted to investigate the properties of both the modified impregnated paper and the decorative panel. The results showed that the thermal stability of the modified resin was improved with a curing temperature of 124 °C. In comparison to the control, the modified impregnated paper showed an increase of 146.0 % in tensile strength and 154.5 % in elongation at break. The improved toughness of the modified MUF-impregnated paper resulted in a notable upsurge in both surface bond strength and cracking resistance of the decorative panel. The combustion test results indicated that the modified impregnated had a LOI value of 40.0 % and self-extinguishing behavior. In addition, due to the inclusion of Nano-Al2O3, the decorative panel exhibited a low abrasion value of only 14.1 mg/100r. Overall, the technology proposed in this study can improve the surface properties of decorative panels, increase their added value, and provide a new strategy for modifying MUF resin in the impregnated paper-decorated wood-based panels industry and for researchers.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: Colloids and Surfaces A: Physicochemical and Engineering Aspects
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.