Abstract
The efficiency of different surface pretreatments (four standard chemical etchings and four diamond powder abrasive procedures) on silicon nitride (Si3N4) substrates for chemical vapor deposition (CVD) of diamond has been systematically investigated. Blank Si3N4 samples were polished with colloidal silica (∼0.25 μm). Diamond nucleation and growth runs were conducted in a microwave plasma chemical vapor deposition apparatus for 10 min and 6 h, respectively. Superior results concerning nucleation density (Nd∼ 1010 cm−2 after 10 min), film uniformity, and grain size (below 2 μm after 6 h) were obtained for the mechanically microflawed samples, revealing that chemical etchings (hot and cold strong acids, molten base or CF4 plasma) are not crucial for good CVD diamond quality on Si3N4.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.