Abstract
A facile solution-based strategy was found to be effective for surface passivation of undoped hematite nanorod photoanodes by adding noble-metal chlorides such as HAuCl4 and H2PtCl6 in the Fe3+ precursor solution. XPS and Raman spectra revealed that noble-metal ions would not be doped into, but lead to surface disorder of hematite. Incident photon to current efficiency (IPCE) of the hematite photoanode grown in HAuCl4 and H2PtCl6 contained precursor solution was increased from 3.6% to 11.5% and 12.9%, respectively, at 365nm and 1.23V vs. RHE (reversible hydrogen electrode). This photoelectrochemical (PEC) enhancement was ascribed to the surface passivation, which resulted in a reduced recombination of photogenerated carriers, as confirmed by ultrafast transient absorption spectroscopy.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.