Surface morphology, microstructure and properties of as-cast AZ31 magnesium alloy irradiated by high intensity pulsed ion beams

Abstract

Abstract High intensity pulsed ion beam (HIPIB) irradiation was performed as surface modification to improve the properties of as-cast AZ31 magnesium (Mg) alloys. The surface morphology and microstructure of the irradiated Mg alloys were characterized and their microhardness, wear resistance and corrosion resistance before and after HIPIB irradiation were measured. The results show that the formation of crater on the surface was attributed to the particles impacted from the irradiated cathode material. HIPIB irradiation resulted in more vacancy defects on the surface of the material. Moreover, new dislocations were generated by the reaction between vacancies, and the dislocation configuration was also changed. These variations caused by the HIPIB are beneficial for improving the material properties. After 10 shots of irradiation, the average microhardness increased by 27.1% but the wear rate decreased by 38.5%. The corrosion rate was reduced by 24.8% according to the salt spray corrosion experiment.