Abstract
The modification of the sputtered NiOx (x ≧ 1)/CH3NH3PbI3 interface by 2-(3,6-dimethoxy-9H-carbazol-9-yl) ethyl] phosphonic acid (MeO-2PACz) considerably enhances the power conversion efficiency of perovskite solar cells whose structure is ITO/NiOx/CH3NH3PbI3/[6,6]-phenyl C61 butyric acid methyl ester (PCBM)/aluminum-doped zinc oxide (AZO)/Ag. In devices without MeO-2PACz, the internal quantum efficiency (IQE) above 450 nm increases with the increase in NiOx thickness from 4 to 53 nm, although even in the thickest case, the IQE never reaches 90%. On the other hand, devices with MeO-2PACz modified NiOx show thickness-insensitive IQE of ca. 90%. We propose that (1) MeO-2PACz effectively fills the pinholes in thinner NiOx and (2) it passivates the carrier trapping/recombination defects at the NiOx/perovskite interface.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.