Abstract
Spinel LiMn2O4was modified with Y2O3coating by a chemical process. The crystal structures of the as-prepared samples were investigated by X-ray diffraction (XRD). The charge/discharge characteristics of the modified samples were evaluated at different rates between 3.0 and 4.4V. The discharge capacities of 2.0 wt.% Y2O3-coated LiMn2O4are 116 mAh•g−1, 99.7mAh•g−1, 93.3mAh•g−1and 82.9mAh•g−1at 0.1C, 0.5C, 1C and 2C rates (at 20◦C). The cycle abilities improvement of the spinel LiMn2O4coated with Y2O3are demonstrated at elevated temperature (55◦C) and high rates (2C). From the analysis of electrochemical impedance spectroscopy (EIS), the improvement of cycle ability may be attributed to the suppression on the formation of the passivating films and the reduction of Mn dissolution, which result from the surface modification with Y2O3.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.