Abstract
Surface modification of poly(vinylidene fluoride) (PVDF) membrane was accomplished by the adsorption of ferric hydroxide sol to impove its hydrophilicity. The adsorption curves of the membranes were analyzed by weight measurements, and the typical results showed a two-platform character in low concentration. The effects of the adsorption time, the ferric hydroxide sol concentration, the test temperature, as well as the water cleaning time on the adsorption amount were observed. Attenuated total reflection-Fourier transform infrared spectroscopy (ATR/ FTIR) analysis showed that the adsorption of ferric hydroxide sol on poly(vinylidene fluoride) microporous membranes (PVDFMM) is effective. The membranes hydrophilic performance was represented by water contact angle measurements. The water contact angles changes from the virgin 128°to the lowest value 81.90° in the range of 0~0.10 mol/L ferric hydroxide aqueous solution. The results indicated that ferric hydroxide sol can be immobilized on the PVDF films by adsorption, and the membrane hydrophilic performence increases with the increase of the adsorption amount of the ferric hydroxide sol onto the PVDF membrane surface.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.