Abstract
The laser irradiation on Al-Si alloy sample is carried out by excimer laser in ambient conditions for 30 or 45 pulses. Microstructural investigation of laser treated sample is done by OM, SEM and TEM and the surface hardness is evaluated by Vickers micro indentation. Laser treated, samples suggested the dissolution of coarse primary Si and β-AlFeSi particle in α-Al matrix. The SEM/EDS study shows the enhancement of retained Si in α-Al matrix. The interface analysis of laser treated sample suggested the effected modified depth is ∼6 μm. TEM investigation shows the formation of nanocrystalline Si in size ∼2–15 nm. The cellular structures of size range ∼30–50 nm are observed after 45 pulses. The α-Al cells and Si precipitates sizes were considerably refined at higher number of pulses. The fine Si precipitates are found to be dispersed in the intercellular boundaries. An improvement in surface hardness from ∼1.6 to 1.8 is observed 30 and 45 pulse treatment, respectively. The mechanism involves for improvement in surface properties are non-equilibrium solidification, metastable phase formation and microstructural refinement.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.