Abstract
AbstractWe investigated the oxygen evolution reaction (OER) activity changes of cobalt oxide (CoOx) thin films on Ir(111) and Pt(111) substrates by repeated OER measurements in 0.1 M KOH. Atomic force microscopy and X‐ray photoelectron spectroscopy analysis of the as‐prepared CoOx/Ir(111) and CoOx/Pt(111) showed similar surface morphologies of the CoOx thin films and almost the same OER overpotentials, which were estimated to be around 430 mV. However, after three OER measurements, the overpotential of CoOx/Ir(111) decreased by 70 mV, whereas that of CoOx/Pt(111) increased slightly. Structural analysis showed that CoOx/Ir(111) revealed the island‐like nanostructures of CoOx dispersed on Ir(111) surface, accompanied by the generation of CoOOH. In contrast, for CoOx/Pt(111), the Pt(111) substrate remains covered by the CoOx thin film. The results suggest that the interaface at CoOx (CoOOH) nano‐islands and Ir(111) substrate are responsible for reducing the OER overpotential.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.