Abstract

Multiwalled carbon nanotubes (MWNTs) were surface photo-oxidized at room temperature with UV (253.7 and 184.9 nm) and vacuum UV (VUV) (106.7 and 104.8 nm) radiation. X-ray photoelectron spectroscopy (XPS) showed rapid UV photo-oxidation during the first hour of treatment and then an increase that was directly proportional to the time of treatment up to 4 h where the oxygen concentration was 7.5 at%. VUV photo-oxidation resulted in an oxygen concentration up to 9.5 at% with exposure time for the initial 2 h of treatment. Beyond 2 h, the oxygen concentration decreased with exposure to VUV photo-oxidation. Curve fitting of the XPS C1s spectra revealed mainly C–O–C, as ether or epoxy functional groups, with the presence of C=O, O–C=O and O=C–O–C=O or carbonate moieties. SEM micrographs showed no apparent effect on the structure or appearance of the MWNTs as expected from surface modification. Gas-phase UV and VUV photo-oxidation effectively functionalize MWNTs for potential adhesion improvement without resulting in liquid waste as from the traditional bulk processing method involving acidic oxidation.

Full Text
Paper version not known

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.