Abstract
ABSTRACTThe aim of this study was to analyze how corona dosages above recommended levels affect film surface energy and hydrophobic recovery of such treated film surfaces as well as laminate bond strength of laminates made of these films. The adhesive for lamination was a polyurethane‐adhesive with a dry film thickness of ∼5 µm. Polar and dispersive parts of the surface energy were measured frequently according to DIN 55660‐2 (Owens–Wendt–Rabel‐and‐Kaelble method) for up to 140 days after corona treatment. The corona dosage had a value of up to 280 W min/m2. Laminate bond strength was measured according to DIN 55543‐5. The effect of corona treatment was highest for low‐density polyethylene (PE‐LD) films, mean for biaxial‐oriented polypropylene (PP‐BO) films, and lowest for biaxial‐oriented poly(ethylene terephthalate) (PET‐BO) films. With increasing storage time, surface energy decreased, as expected. The higher the effect of corona treatment, the faster the polar part of surface energy decreased. At PE‐LD, laminate bond strength increased with a higher corona dosage from 0.05 to 8.87 mN/15 mm, whereas at PET‐BO and PP‐BO laminate bond strength was so high that samples teared before delamination during bond strength testing. By our results is shown that corona dosages above recommended levels resulted in higher laminate bond strength. Only at PP‐BO a reduction of laminate bond strength due to “overtreatment” was be observed. © 2017 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2018, 135, 45842.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.