Abstract
Surface dilatational moduli of poly(vinyl acetate) (PVAc) film and blend films of PVAc and poly(n-hexyl isocyanate) (PHIC) were measured at the air-water interface. PVAc formed a film that was looser and also more stable against strain than the PHIC film. The apparent surface dilatational modulus and surface pressure of the blend films were superimposed on the lower concentration of PVAc, irrespective of the composition of PVAc. However, the additivity rule was not applicable to the apparent surface dilatational modulus and surface pressure. The scaling exponents of the apparent surface dilatational modulus against the added surface concentration decreased with an increase in the proportion of PVAc, suggesting that blend films gradually change from glass material to expanded films.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.