Surface Crystallization and Water Diffusion of Silica Glass Fibers: Causes of Mechanical Strength Degradation

Abstract

Pristine silica glass fiber is well‐known to become mechanically weaker when heat‐treated in air but the cause of such weakening is not presently known. The time dependence of mechanical degradation of various silica glass fibers containing varying impurity contents were studied in the range from 500°C to 1000°C. Two possible sources of strength degradation were considered: surface crystallization and water diffusion. Surface crystallization kinetics of silica glass fibers were investigated in a wide temperature range, including nanoscale surface nucleation at low temperatures via scanning electron microscopy. From the comparison of the strength degradation, surface crystallization, and water diffusion data in literature, it was concluded that surface crystallization may be responsible for the mechanical weakening observed in silica glass fiber surface during heat‐treatment at temperatures above ~800°C, whereas water diffusion into the glass surface may be responsible for the strength degradation at lower temperatures.