Abstract
Colloidal CdSe nanocrystals were synthesized through a solution process. The CdSe nanocrystals coated on Si(1 0 0) wafers were UV-exposed in either an air or argon atmosphere to distinguish the effect of generated ozone from UV-radiation at 365 nm on the removal of surface capping pyridine molecules. The pyridine on the CdSe nanocrystal's surface could be effectively removed by the ozone generated during UV-exposure with an accompanying highly oxidized surface state of the CdSe nanocrystals. For the removal of surface oxides of CdSe nanocrystals, a successive thermal treatment under ultra high vacuum (UHV) was adopted. The optical energy bandgap measured by using UV–vis absorption spectroscopy showed a red shift with treatment with an increase of annealing temperature. The electronic energy structure of UHV-annealed CdSe nanocrystals film was analyzed in situ using X-ray absorption and photoelectron spectroscopy. A great resemblance was found between the values of the optical and electron energy bandgaps of effectively surface-treated CdSe nanocrystals film after UHV-annealing at 400 °C.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.