Abstract

Sintered alumina samples of grain diameters spanning from 1.2 to 4.5 μm have been investigated by positron annihilation lifetime spectroscopy. One series of samples was produced from material containing about 150 ppm impurities (mainly SiO 2 ). The second one was made from material having about 2700 ppm of various elements (SiO 2 , MgO, CaO). Two models of positron trapping at grain boundaries are compared: The first one relates to the diffusion-limited regime; and the other one - to the transition-limited regime of trapping. As a result the relative change of surface concentration of defects at grain boundaries is determined. Additionally, the positron diffusion constant in bulk alumina at room temperature, D + = 0.36 ′ 10 cm 2 /s, is estimated.

Full Text
Paper version not known

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.