Abstract
Four La-Fe oxide samples with La/Fe atomic ratio y=1.02∼0.68 (denoted as LayFe) were prepared by the citrate method. The samples had a decreased specific surface area with the La/Fe atomic ratio decreasing. XRD pattern proved that the sample La0.94Fe is single phase perovskite La0.94FeO3−d. Phase composition of the samples was estimated by the Rietveld refinement method. XPS analyses indicate that La3+ ions are enriched on surface of crystallites for all the samples, and surface carbonate ions are relatively abundant on the samples La1.02Fe and La0.94Fe. Catalytic activity for methane oxidation per unit surface area of the samples is in the order of La0.68Fe>La0.76Fe>La0.94Fe>La1.02Fe both in the presence and in the absence of gaseous oxygen. A reason for this order would be the higher concentration of Fe3+ ion on the surface of the samples La0.68Fe and La0.76Fe.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.