Abstract
The present study focused on evaluation of anodized oxides prepared in four mixed acid electrolytes with and without phosphoric acid as a function of forming voltage. Specifically the oxide surface characteristics, the mechanical integrity, and the bioactive performance were evaluated for a range of forming voltages in each electrolyte. Surface analyses showed phosphorus incorporation into the oxide layer started at localized areas after a threshold forming voltage, but became more uniform at higher voltages. Oxide crystallinity and thickness were retarded by the phosphoric acid levels present in the anodization electrolytes. Surface roughness was shown to be electrolyte dependent as a function of forming voltage, and in general was shown to increase with increasing voltage. Samples anodized up to a forming voltage of 144V did not show any oxide failure through shear strength testing with only epoxy delamination for three of the electrolytes. At 180V, the oxide layers showed failure or partial failure at approximately 30–35MPa, which is stronger than many values previously reported for anodized coatings in the literature. Additionally, oxide films prepared in phosphoric acid containing electrolytes showed greater bioactivity through enhanced apatite formation. These anodized coatings exhibiting enhanced bioactivity show promise for promoting faster osseointegration while providing better implant stability due to the superior coating adhesion strengths.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.