Abstract
The surface characteristics and fatigue performance of the warm shot peened Mg–9Gd–2Y alloys were investigated. Compared to conventional shot peening (SP) at room temperature, warm shot peening (WSP) at 240°C induces higher subsurface hardening and larger maximum compressive residual stress in the subsurface of the specimens. The optimum Almen intensity of WSP is 0·15 mm N, whereas it is 0·10 mm N for SP. The main reason is that the surface of warm shot peened specimen is more plastically deformed but less damaged at the optimum Almen intensity due to the increase in plastic deformation ability of the tested alloys at elevated temperature. The fatigue strength of the tested alloy at 107 cycles is increased from 125 to 175 MPa by optimum SP and to 185 MPa by optimum WSP.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.