Abstract
The FeCoNiCrMo0.2 high entropy alloy coatings were deposited on BS960 high strength steel by plasma spraying method with four different current intensities (250 A, 350 A, 450 A, 550 A). These coatings were then subjected to a subsequent micro-shot peening treatment. Surface characteristics including surface morphology, microhardness and phase composition were characterized, and the wear resistance of the coatings was assessed by reciprocal friction and wear tests. The results showed that the high entropy alloy coatings had FCC structure. XRD results showed that no new phase was formed during the spraying process. At the same time, shot peening treatment could effectively improve the hardness of the coating surface. Under the four processes, the coating surface prepared with the current intensity of 350 A had the highest microhardness and uniformity before and after shot peening, and the hardness values were 473 ± 10.21 and 504 ± 8.62 HV0.2, respectively. The friction and wear test results showed that the friction coefficients of the four coatings were close to each other at 10 N load, which was about 0.4. When the test load reached 25 N, the friction coefficient of the coating with current intensity of 350 A was lower, and it showed better friction performance. After shot peening, the friction coefficient of the four coatings further decreased to about 0.3 under 10 N loading due to the existence of hardened surface layer. When the test load reached 25 N, the hardened layer would be worn through and the friction coefficient would suddenly rise. Under the 25 N test load, the hardened layer of the high-entropy alloy coating with current intensity of 350 A illustrated better friction resistance.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.