Abstract
The surface oxides formed during oxidation of Al alloys for automobile body panels were analysed using electron spectroscopy for chemical analysis, Auger electron spectroscopy, and energy dispersive X-ray spectrometry. Two commercial AA 6000 alloys were studied. The alloys were oxidised in dry air at room temperature, 300°C, 400°C, and 520°C. The thicknesses and the compositions of the oxides formed on the matrix and on the Si, Mg2Si, and Al–Fe–Si particles were determined. The surface oxides consist primarily of Al2O3 and MgO. The content of MgO increases with temperature. The activity of Mg is decreased owing to formation of Mg2Si at the metal/oxide interface during oxidation. A model for the formation and growth of MgO nodules at high temperatures is proposed; during the initial stages of oxidation Al2O3 is formed, and after prolonged exposure the oxide cracks and Mg evaporates. Magnesium oxide is formed on the surface by condensation and oxidation of Mg. One piece of evidence for this mechanism is that MgO is found on the non-Mg containing Si and Al–Fe–Si particles.MST/3348
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.