Abstract
ABSTRACTWe have prepared supramolecular polymer gels by mixing solutions of a polystyrene bearing cyclic amidine pendant groups (Poly‐A) and copolymers of acrylic acid and n‐butyl acrylate (Poly‐C), followed by evaporation. FT‐IR analysis indicated that the gels were formed through three‐dimensional network of the amidinium‐carboxylate salt bridge. DSC study showed that the Poly‐A and the Poly‐C were miscible when the salt bridge content was high. On the other hand, the mixtures with small salt bridge content showed phase separation. Dynamic shear measurements showed that the gel prepared from Poly‐A and Poly‐C with acrylic acid unit content of 15% had G' higher than G″ over a temperature range of −22 °C to 32 °C, in which the G' value reached almost 1 MPa. The gel had a crossover point of G' and G″ at 32 °C, very close to room temperature, which suggested facile processability. © 2015 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2016, 54, 765–770
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of Polymer Science Part A: Polymer Chemistry
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.