Abstract
Thin films made of weak polyelectrolytes poly(allylamine hydrochloride) (PAH) and poly(acrylic acid) (PAA) have been fabricated on silicon wafers using the layer-by-layer (LbL) method. To study the influence of counteranion type on the growth and properties of PAH/PAA multilayers, the nature of the supporting sodium salt was varied from cosmotropic to chaotropic anions (F-, Cl-, and ClO4 -). Results of ellipsometry and AFM measurements indicate that the film thickness and surface roughness systematically increase on the order F- < Cl- < ClO4 -. Furthermore, we found that the hydrophobicity of the PAH/PAA multilayer also follows the described trend when a polycation is the terminating layer. However, the heating of PAH/PAA multilayers to 60 °C during the LbL assembly suppressed the influence of background anions on the multilayer formation and properties. On the basis of the obtained results, it could be concluded that thermal annealing induces changes at the polymer-air interface in the sense of reorientation and migration of polymer chains.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.