Abstract
The phase changes in alkali-activated slag samples when exposed to supercritical carbonation were evaluated. Ground granulated blast furnace slag was activated with five different activators. The NaOH, Na2SiO3, CaO, Na2SO4, and MgO were used as activators. C-S-H is identified as the main reaction product in all samples along with other minor reaction products. The X-ray diffractograms showed the complete decalcification of C-S-H and the formation of CaCO3 polymorphs such as calcite, aragonite, and vaterite. The thermal decomposition of carbonated samples indicates a broader range of CO2 decomposition. Formation of highly cross-linked aluminosilicate gel and a reduction in unreacted slag content upon carbonation is observed through 29Si and 27Al NMR spectroscopy. The observations indicate complete decalcification of C-S-H with formation of highly cross-linked aluminosilicates upon sCO2 carbonation. A 20–30% CO2 consumption per reacted slag under supercritical conditions is observed.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.