Superconducting Properties of Mg$_{2}$Cu-Doped MgB$_{2}$ Wires With Several Metal Sheath for Fusion Reactor Application

Abstract

The advantages of MgB <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> compound for a future fusion reactor application are not only high T <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">c</sub> (39 K) and low cost but also low activation material. MgB <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> compound is non Nb-based superconductor and its decay time of induced radioactivity may be about 10 years and significantly shorter than Nb-based superconductors. In this paper, we fabricated the Mg <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> Cu doped MgB <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> wires using several metal sheath materials to improve J <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">c</sub> property. The selection of metal sheath materials is also important to apply for fusion reactor. Pure Fe, Ta and Cu have faster decay time of induced radioactivity compared the other metals. T <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">c</sub> values of all Mg <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> Cu doped samples were higher than those of non-doping samples, and T <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">c</sub> values were improved with increasing amount of Cu doping. And the maximum core-J <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">c</sub> value was estimated to be 100 A/mm <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sup> over at 4.2 K under 8 T for 3 at% Cu doping sample. The comparisons of superconducting property between different metal sheath materials are discussed.