Abstract
Nominally pure and B2O3-added (Bi,Pb)-2223 HTS samples were synthesized in air on alumina plates. The influence of boron-doping as well as annealing conditions on the high-Tc 2223 phase evolution was studied using X-ray diffraction (XRD), resistivity and AC susceptibility measurements. The B2O3-added samples with starting composition Bi1.7Pb0.3Ca2Sr2Cu3BxOy (x=0.05 and 0.5) reveal significant enhancement of 2223 phase formation compared to the undoped sample. Higher-level boron doping x=1.5 leads to the degradation of high-Tc 2223 phase.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.