Abstract
Superconducting Ba1−xKxBiO3 (BKBO) thin films and heteroepitaxial multilayers were deposited by in situ off-axis sputtering on various substrate at 400 °C. A typical superconducting BKBO thin film on the SrTiO3 and MgO substrates had a very sharp zero resistance transition at a temperature of 22–24 K as measured by transport four point and mutual inductance probes. The normal state resistivity exhibited metallic to semiconductive characteristics depending on film composition with the lowest room temperature resistivity of about 0.25 mΩ cm. The film orientation was highly epitaxial to both SrTiO3 and MgO substrates. Normal metal-insulator-superconductor (NIS) type tunnel functions with native insulator layer and deposited MgO layer were reproducibly fabricated. The superconducting energy gap of about 3.6 meV was obtained from those NIS junctions. Heteroepitaxial superconductor- insulator-superconductor (SIS) trilayer junctions were also fabricated using MgO insulator layers. For a 5 nm thick insulator layer, quasiparticle SIS tunnel junctions with nonhysteric I-V characteristics were obtained. By reducing MgO insulator layer thickness down to 3 nm, SIS tunnel junctions with Josephson supercurrent were obtained with hysteric I-V characteristics.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.