Abstract
AbstractS‐allyl‐4‐methyldithiobenzoate was synthesized and used as a chain transfer agent for the RAFT polymerization of butyl acrylate to produce a functionalized acrylic rubber. A solution of 8 wt% of this functionalized rubber was prepared in styrene and polymerized to generate a material called acrylic rubber‐modified polystyrene (AMP) constituted by well‐dispersed particles of poly(butyl acrylate)‐block‐poly(styrene) into a polystyrene matrix. Impact strength of injection‐molded samples of AMP was measured and compared with the general purpose polystyrene (GPPS) and the high impact polystyrene (HIPS). AMP itself showed an impact strength value similar to GPPS; however, when AMP was blended with conventional HIPS, the resulting material exhibited an improvement of 76–91% as compared to HIPS by itself, without affecting negatively tensile properties. Transmission electron microscopy analysis revealed both kinds of dispersed phases, i.e. the typical salami particles of polybutadiene coming from HIPS (size: 0.5–2 µ) and small particles from poly(butyl acrylate)‐block‐poly(styrene) (size: ∼50 nm). We clearly showed that such a bimodality of the particle size distribution caused the positive synergistic effect on impact strength. Copyright © 2011 John Wiley & Sons, Ltd.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.