Sulfur-Rich Additive-Induced Interphases Enable Highly Stable 4.6 V LiNi0.5Co0.2Mn0.3O2||graphite Pouch Cells.

Abstract

High-voltage lithium-ion batteries (LIBs) have attracted great attention due to their promising high energy density. However, severe capacity degradation is witnessed, which originated from the incompatible and unstable electrolyte-electrode interphase at high voltage. Herein, a robust additive-induced sulfur-rich interphase is constructed by introducing an ultrahigh S-content of 34.04% additive (methylene methyl disulfonate, MMDS) in 4.6 V LiNi0.5Co0.2Mn0.3O2 (NCM523)||graphite pouch cell. The MMDS does not directly participate the inner Li+ sheath, but the strong interactions between MMDS and PF6- anions promote the preferential decomposition of MMDS and broaden the oxidation stability, and facilitate the formation of an ultrathin but robust sulfur-rich interfacial layer. The electrolyte consumption, gas production, phase transformation and dissolution of transition metal ions were effectively inhibited. As expected, the 4.6 V NCM523||graphite pouch cell delivers a high capacity retention of 87.99% even after 800 cycles. This work shares new insight into the sulfur-rich additive-induced electrolyte-electrode interphase for stable high-voltage LIBs.