Abstract
The sulfide capacityC S 2- = (pct S2-) · (P O 2/P S 2)1/2) of CaO-CaF2-SiO2 slags saturated with CaO, 3CaO · SiO2 or 2CaOSiO2 was determined at 1200 °C, 1250 °C, 1300 °C, and 1350 °C by equilibrating molten slag, molten silver, and CO-CO2 gas mixtures. Higher sulfide capacities were obtained for CaO-saturated slags. A drastic decrease was observed in those values when the ratio pct CaO/pct SiO2 is less than 2. The sulfur partition between carbon-saturated iron melts and presently investigated slags was calculated by using the sulfide capacities obtained and the activity coefficient of sulfur in carbon-saturated iron, which was also experimentally determined. For slags saturated with CaO, partitions of sulfur as high as 10,000 were obtained at 1300 °C and 1350 °C. Correlations between the sulfide capacity and other basicity indexes such as carbonate capacity and theoretical optical basicity were also discussed.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.