Abstract
The paper describes the production of an AlSi7Mg cast alloy with Li additions and the reactions of the melt with different moulding materials. It is known that Li is very reactive and tends to form various reaction products such as oxides, gases, etc., which can influence the casting quality. The aim of the research was to find a suitable way to produce such an alloy and to describe the reaction products that are formed between the melt and the moulding material and thus to find a suitable moulding material for processing Al cast alloys with Li additions. The melt was produced in an induction furnace under an inert atmosphere. After melting, 1 w/% Li was added and the melt was cast into five different mould materials consisting of graphite, steel, a CO2 sand mixture, Croning mixture and calcium silicate materials. In the last three cases, various alcohol-based coatings were also used, such as graphite, zirconium oxide-graphite coating and aluminate-graphite filler coating. The results showed that the reaction products in the form of powder on the casting surfaces and the gas porosity in the castings occurred in the cast of a calcium silicate mould and sand mould mixtures. In the case of graphite and steel moulds, the casting surfaces were not oxidised, with no reaction products, and no gas porosity.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.