Abstract
Abstract The hereby work presents the iron-nickel alloys electroplated on the different metallic substrates (aluminium, silver, brass) using galvanostatic deposition, with and without presence of the external magnetic field (EMF). The films were obtained in the same electrochemical bath composition - mixture of iron and nickel sulphates (without presence of additives) in the molar ratio of 2 : 1 (Ni : Fe), the electric current density (50.0 mA/cm2), and the time (3600 s). The mutual alignment of the electric (E) and magnetic field (B) was changeable - parallel and perpendicular. The source of EMF was a set of two permanent magnets (magnetic field strength ranged from 80 mT to 400 mT). It was analysed the surface microstructure, composition, morphology, thickness and the mechanical properties (roughness, work of adhesion). The surface morphology and the thickness of films were observed by Scanning Electron Microscopy (SEM) and Confocal Laser Scanning Microscopy (CLSM). The elemental composition of all FeNi films was measured using Wavelength Dispersive X-Ray Fluorescence (WDXRF). The crystalographic analysis of the deposits was carried out by X-Ray Diffraction. Depending on the used substrate, modified external magnetic field orientation influenced the tribological and physio-chemical properties of the deposited layers. The diamagnetic substrates and EMF application reduced the FeNi thickness and the average crystallites size, in contrast to the paramagnetic substrate. Parallel EMF increased the value of the tribological parameters for CuZn and Ag but decreased for Al. The content of FeNi structure was rising in the case of diamagnetic substrate and the dependence was opposite on the paramagnetic substrate.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.