Abstract
We deployed a 2kW continuous wave fiber laser integrated with the 5-axis workstation to understand the effect of various processing parameters (laser power, welding speed, beam spot size and chamfer at welded edges) on depth of penetration, angular distortion and welded bead surface profile during autogenous laser welding of 6mm thick austenitic stainless steel type 304 plates. Full penetration with reduced weld bead surface undulation (<100µm) and least angular distortion (<0.8°) was achieved for butt joints having chamfered edges of 0.8mm. The microscopic studies revealed grossly defect-free fusion zone with a few porosities at isolated locations. The microstructure at the fusion zone was largely austenitic with few ferrites and the direction of growth was epitaxial towards the fusion line. The measured values of microhardness at base material and fusion zone were 208±4 HV0.1 and 235±10 HV0.1 respectively. The tensile testing of laser welded samples indicated the ultimate strength >605MPa and these samples could be bent for an angle >170° without noticeable crack during bend test. The study opened the avenues for the deployment of fiber laser welding technology for applications demanding critical values of surface weld bead profile and distortion.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.