Abstract
Spent catalysts for sulfuric acid production have large amount of vanadium and due to environmental authority it is required to reduce the vanadium contain of the spent catalyst. Experimental investigation was conducted to study the vanadium recovery from spent catalyst via leaching process using sodium hydroxide to study the effect of process variables (temperatures, sodium hydroxide molarities, leaching time and particle size) on vanadium recovery. The effect of process variables (temperature, particle size,molarities of sodium hydroxide and leaching time) on the percentages of vanadium recovery were investigated and discussed .It was found that the percentage of vanadium recovery increased with increasing temperature up to 100 , increasing sodium hydroxide molarity from 2 to 4M, increasing leaching time, decreasing particle size from mesh 150, 100 and 65. A complete vanadium recovery was achieved at the following conditions: temperature (100˚c), particle size (150 mesh ) molarity of Na OH(4 molar) and leaching time(5 h).
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Iraqi Journal of Chemical and Petroleum Engineering
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.