Abstract
Hand layup was used to fabricate the glass fibre reinforced aluminium foam epoxy composites in this study. On the manufactured materials, dry sliding wear experiments were performed. The effect of wearprocess parameters such asapplying load (kg), speed (m/s), and sliding distance (m) on specific wear rate (Ws) was investigatedand the obtained results were compared with neat glass fibre reinforced epoxy composite in this work. The outcome of these results showed that specific wear rate (Ws) of glassfibre epoxy composite containing aluminium foam decreased as compared with neat glass fibre reinforced polymer composites. Experimental results showed that a minimum wear rate of 10.1 �m was attained for the sliding velocity (1.5 m/s), Applied load (2 kg), and sliding distance (1000 m) in the fabricated composite laminates. It was observed thatthe resistance to wear in glass fibre reinforced aluminium foam composite was mainly due to the bond strength between aluminium foam and epoxy.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.