Abstract
This paper reports on the successful preparation of a low absorption–emission thermal control coating on the surface of LAZ933 magnesium–lithium alloy using the micro-arc oxidation method. This study analyzed the microstructure, phase composition, and thermal control properties of the coating using Scanning Electron Microscopy (SEM), X-ray diffraction (XRD), UV–visible near-infrared spectroscopy (UV-VIS-NIR) and infrared emissivity measurements. The results indicate that the hemispherical emissivity of the coating remains unaffected with an increase in temperature and holding time, while the solar absorption ratio gradually increases. The thermal control performance of the coating after a high-temperature experiment was found to be related to the diffusion of the Li metal element in the magnesium lithium alloy matrix, as determined by X-ray photoelectron spectroscopy (XPS), flame graphite furnace atomic absorption spectrometry (GFAAS) and Glow Discharge Optical Emission Spectroscopy (GD-OES). As the holding time is extended, the coating structure gradually loosens under thermal stress. The Li metal element in the substrate diffuses outward and reacts with O2, H2O and CO2 in the air, forming LiO2, LiOH, Li2CO3 and other products. This reaction affects the coating’s solar absorption ratio in the end.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.