Study on the packing density of structurally modified ring spun yarn

Abstract

Fibres being the structural unit of a yarn, its nature, composition and arrangement can influence structure and properties. The performance of yarn changes with arrangement of its constituent fibres. Arrangement of fibres in a yarn being system specific, different spinning system results different arrangement of fibres causing variation in product performance. A change in the arrangement of fibres in an already formed yarn can be brought about by suitable physical and/or chemical treatment. A treatment to remove a component is expected to cause changes in final arrangement of fibres in a yarn. In the present study, polyester/PVA blended yarn was modified through dissolution of the later component. The resultant change in structural arrangement on dissolution was assessed by the change in radial packing distribution of fibres. Migration index, helped in identifying the location that was influenced more in the redistribution. In the parent yarn, PVA had a preferential tendency to predominate near the core. On dissolution of PVA, creation of open space was expected and collapsing of the structure led to a possible rearrangement of fibres and reduction in diameter of yarn. Fibre denier, blend ratio and twist factor were also found to influence packing density both in parent and modified yarn. Unlike published reports, interestingly, an increase in fibre packing density was observed on dissolution of PVA. Average packing density in parent yarn was found to lie at a yarn radius between 0.07 mm to 0.09 mm while for the modified yarn it was between 0.05 mm to 0.07 mm.