Abstract

The influence of different ceramsite pre-wetting time and the floating beads content on the properties of lightweight high-strength concrete was studied in this paper. The results showed that as the pre-wetting time increased, the absorption rate of ceramsite continued to increase, reaching a saturated state at 12 h with 36.14% water absorption rate; the concrete slump/expansion degree is increased significantly, and the growth rate decreased gradually, and the improvement was not obvious after 12 h; the 7 d strength of concrete saw an obvious downturn, and the strength dropped by 10.4% at 12 h, after which the decline was basically stable; the 28 d strength, 28 d strength growth rate and 7 d-28 d strength growth rate all showed a steady upward trend, which reached 61.18 MPa, 12.4% and 29.73% respectively at 12 h, and the growth rate was basically stable afterwards; as the floating beads content increased, the concrete dry density, slump/expansion degree, 7 d and 28 d strength all showed a significant decline trend.

Full Text
Paper version not known

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.