Abstract
Several studies have been conducted on the fatigue behavior of copper and 7-3, and 6-4 brasses. However, there have been fewer studies on the fatigue behavior and fatigue crack growth (FCG) properties of free-cutting brass, primarily because emphasis has been placed on the development of lead-free free-cutting brass. In this study, fatigue experiments were performed in the atmosphere at room temperature using three types of free-cutting, two types of bismuth (Bi)-based (with different grain sizes), and lead (Pb)-based brasses. It was found that lead-free Bi-based free-cutting brass had approximately the same fatigue performance as that of Pb-based free-cutting brass. It was also clarified that the addition of Bi or Pb initiated fatigue cracks, and that the crack growth period occupied most of the fatigue life. Differences in the FCG behavior of the three free-cutting brasses were observed in the low ΔK range. The modified linear fracture mechanics parameter M was used to quantitatively analyze the fatigue life and FCG behavior (short surface cracks). A comparison between the calculated and experimental results showed that M was useful.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.