Abstract
P92 steel is candidate material for application in reactor pressure vessels in nuclear power plants. In present investigation, Laves phase evolution (at 650°C) with varying ageing time (upto 3000h) in P92 steel and their effect on mechanical properties have been investigated. During thermal ageing, the microstructure analysis showed the evolution of Laves phase that degrades the strength of P92 steel. The formation of Laves phase was observed after the thermal ageing of 720h and it showed higher coarsening rate in ageing time range of 720h −1440h. The Laves phase formation was also confirmed by the XRD analysis, and line mapping. The strength and ductility decreased as a result of deprivation of solid solution strengthening and formation of Laves phase. The hardness of P92 steel was also affected by ageing time but less pronounced as compared to strength. Charpy toughness was also reduced continuously with increase in ageing time as a result of thermal straining of particles and Laves phase formation.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.